| Mowinyl 106E |
Mowinyl 109E |
Mowinyl 6880 |
Mowinyl DM758 |
Mowinyl 7700* |
Mowinyl 7800* |
|
|---|---|---|---|---|---|---|
| Cement-based primer (Mortar admixture) |
● | ● | ● | ● | ||
| Water absorption adjuster for mortar | ● | ● | ● | |||
| Self-leveling compound | ▲ | |||||
| Tile adhesive | ▲ | ■ | ■ | |||
| Repair mortar (chemical-resistant, oil-resistant cement-based material) |
● | |||||
| Elastic mortar | ● | |||||
| Plaster compound | ▲ | ▲ | ■ | ■ | ||
| Hydration setting type coating film waterproofing | ● | |||||
| Concrete admixture | ● |
| Product name | Emulsion properties | Characteristics | Major applications | ||||
|---|---|---|---|---|---|---|---|
| Main content(s) | Non-volatile content (%) |
Viscosity (mPa·s) |
pH | Ionicity | |||
| 106E | Ethylene/vinyl acetate | 45.0 | 1,500～2,500 | 4.5～6.5 | N | Improvement in adhesive force, bending strength, and wear resistance | Water absorption adjuster for mortar, mortar admixture |
| 109E | Ethylene/vinyl acetate | 55.0 | 1,100～1,700 | 4.5～6.5 | N | Improvement in adhesive force, bending strength, and wear resistance | Mortar admixture |
| 7700 | Acryl | 45.0 | 100～800 | 3.5～6.0 | N | Easy to trowel, improvement in adhesive force | Mortar admixture (cement-based primer, etc.), tile adhesive (cement-based, non-cement-based), water absorption adjuster for mortar |
| 7710 | Acryl | 23.0 | 100 or below | 4.0～6.0 | N | Easy to trowel, improvement in adhesive force, for construction sites | Mortar admixture (cement-based primer, etc.), tile adhesive (cement-based, non-cement-based), water absorption adjuster for mortar |
| 7800 | Acryl | 45.0 | 300 | 3.8～5.0 | C | Cation type, easy to trowel, improvement in adhesive force | Mortar admixture (cement-based primer, etc.), tile adhesive (cement-based, non-cement-based), water absorption adjuster for mortar |
| 7810 | Acryl | 23.0 | 100 or below | 4.0～6.0 | C | Cation type, easy to trowel, improvement in adhesive force | Mortar admixture (cement-based primer, etc.), tile adhesive (cement-based, non-cement-based), water absorption adjuster for mortar |
| 7901 | Acryl | 40.0 | 100 or below | 7.5～9.0 | A | Improvement in adhesion to concrete beds, alkali resistant, prevention of lifting and cracking | Primer for concrete |
| LDM6880 | Styrene/acryl | 50.0 | 200 or below | 7.0～9.0 | A | Improvement in durability and compressive strength, significant improvement in chemical and oil resistance, prevention of neutralization | Concrete admixture |
| 6485 | Styrene/acryl | 55.0 | 500～3,000 | 6.5～9.5 | A | Improvement in elongation and waterproof performance | Mortar admixture, coating film waterproofing |
| 7955 | Acryl | 52.0 | 1,000～3,500 | 7.0～9.5 | A | Improvement in elongation and waterproof performance, soap free | Mortar admixture, coating film waterproofing |
| DM758 | Acryl | 60.0 | 4,000～11,000 | 6.5～8.5 | A | Improvement in elongation, elastic at low temperature, less sensitive to temperature | Elastic mortar, mortar waterproofing, repair mortar |
| ES-330 | Acryl | 45.0 | 50～700 | 5.0～7.0 | C | Keeps polymer cement paste viscosity stable, no retardation in cement hardening, soap free | For cement admixture |
| ES-52 | Acryl | 43.0 | 1,000 or below | 1,000 or below | A | Excellent in waterproof performance, weather resistance, chemical resistance, and stability when mixed with other materials | For polymer cement mortar, vehicle for exterior coatings |
| ET-342 | Acryl | 60.0 | 1,000～5,000 | 4.5～7.5 | C | Improves the leveling performance of polymer cement, high in freeze-thaw stability | For cement admixture |
| CS-1 | Acryl | 60.0 | 30000 | 5.5 | A | Excellent in water resistance, chemical resistance, and miscibility with pigments | Water-based caulking |
| CS-10 | Acryl | 60.0 | 5500 | 5 | A | Excellent in water resistance and alkali resistance, conforming to JIS A5738 | Water-based caulking |
| CS-70 | Acryl | 71.0 | 15000 | 6.5 | A | Concentrated type of CS-10 | Water-based caulking |
Ionicity: A: anion N: non-ionic C: cation
*Figures in tables are representative figures only and are not specifications.